KetaSpire® KT-880 GF30

聚醚醚酮

Solvay Specialty Polymers

Technical Data

 

产品说明

KetaSpire® KT-880 GF30 is the high-flow, 30% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire® PEEK resin. Reinforcement also affords greater mechanical robustness in structural applications, particularly those with service temperatures approaching 300°C.

 

KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases.

 

These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses.

 

• Beige: KT-880 GF30 BG 20

• Black: KT-880 GF30 BK 95

总体

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet

UL 黄卡 2 • E140728-100211985

搜索 UL 黄卡 •  Solvay Specialty Polymers

•  KetaSpire®

供货地区 • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

填料/增强材料 • 玻璃纤维增强材料, 30% 填料按重量

• 尺寸稳定性良好 • 好的消毒性 • 耐蒸汽

• 电子束消毒 • 环氧乙烷消毒

• 放射性可透的 • 抗伽马辐射 • 热消毒

特性 • 辐射消毒 • 流动性高 • 生物兼容性

• 刚性，高 • 耐化学性良好 • 用蒸汽消毒

• 高强度 • 耐疲劳性能 • 阻燃性

• 高压锅消毒 • 耐热性，高

• 薄膜 • 连接器 • 医疗/护理用品

• 泵件 • 密封件

用途 • 电气/电子应用领域 • 石油/天然气用品 • 医疗器材

• 飞机应用 • 外科器械 • 医疗器械

• 工业应用 • 牙齿应用领域

机构评级 • FAA FAR 25.853a 3 • ISO 10993 4 • MIL P-46183 Type II Class 3

RoHS 合规性 • RoHS 合规

外观 • 浅米色

形式 • 粒子

加工方法 • 机器加工 • 型材挤出成型 • 注射成型

物理性能 干燥 调节后的 单位制   测试方法

密度 / 比重 1.53 1.53 (g/cm³) ASTM D792

熔流率（熔体流动速率） (400°C/2.16 kg) 14 14 g/10 min ASTM D1238

收缩率 6 ASTM D955

流动 : 0.125 in (3.18 mm) 1.0E-3 到 3.0E-3 1.0E-3 到 3.0E-3 in/in

(0.10 到 0.30) (0.10 到 0.30) (%)

横向流动 : 0.125 in (3.18 mm) 0.013 到 0.015 0.013 到 0.015 in/in

(1.3 到 1.5) (1.3 到 1.5) (%)

吸水率 (24 hr) 0.10 0.10 % ASTM D570

 

 

 

KetaSpire® KT-880 GF30

聚醚醚酮

Solvay Specialty Polymers

机械性能 干燥 调节后的 单位制 测试方法

拉伸模量

-- 7 1.56E+6 1.56E+6 psi ASTM D638

(10800) (10800) (MPa)

-- 1.62E+6 1.62E+6 psi ISO 527-2/1A/1

(11200) (11200) (MPa)

拉伸应力

屈服 25200 25200 psi ISO 527-2/1A/5

(174) (174) (MPa)

-- 23500 23500 psi ASTM D638

(162) (162) (MPa)

伸长率

断裂 7, 8 3.1 3.1 % ASTM D638

断裂 3.1 3.1 % ISO 527-2/1A/5

弯曲模量

-- 1.53E+6 1.53E+6 psi ASTM D790

(10500) (10500) (MPa)

-- 1.54E+6 1.54E+6 psi ISO 178

(10600) (10600) (MPa)

弯曲强度

-- 37700 37700 psi ASTM D790

(260) (260) (MPa)

-- 34700 34700 psi ISO 178

(239) (239) (MPa)

压缩强度 26500 26500 psi ASTM D695

(183) (183) (MPa)

剪切强度 13700 13700 psi ASTM D732

(94.4) (94.4) (MPa)

冲击性能 干燥 调节后的 单位制 测试方法

悬壁梁缺口冲击强度

-- 1.8 1.8 ft•lb/in ASTM D256

(96) (96) (J/m)

-- 5.2 5.2 ft•lb/in² ISO 180

(11) (11) (kJ/m²)

无缺口悬臂梁冲击

-- 16 16 ft•lb/in ASTM D4812

(850) (850) (J/m)

-- 30 30 ft•lb/in² ISO 180

(62) (62) (kJ/m²)

硬度 干燥 调节后的 单位制 测试方法

洛氏硬度 (M 级) 105 105 ASTM D785

热性能 干燥 调节后的 单位制 测试方法

载荷下热变形温度 (264 psi (1.8 MPa), 退火) 599 599 °F ASTM D648

(315) (315) (°C)

玻璃转化温度 297 297 °F ASTM D3418

(147) (147) (°C)

熔融峰值温度 650 650 °F ASTM D3418

(343) (343) (°C)

线形热膨胀系数 - 流动 1.1E-5 1.1E-5 in/in/°F ASTM E831

(-58 到 122°F (-50 到 50°C)) (1.9E-5) (1.9E-5) (cm/cm/°C)

比热 DSC

122°F (50°C) 0.306 0.306 Btu/lb/°F

(1280) (1280) (J/kg/°C)

392°F (200°C) 0.406 0.406 Btu/lb/°F

(1700) (1700) (J/kg/°C)

导热系数 2.1 2.1 Btu•in/hr/ft²/°F ASTM E1530

(0.30) (0.30) (W/m/K)

 

KetaSpire® KT-880 GF30

聚醚醚酮

Solvay Specialty Polymers

电气性能 干燥 调节后的 单位制 测试方法

表面电阻率 > 1.9E+17 > 1.9E+17 ohms ASTM D257

体积电阻率 3.8E+17 3.8E+17 ohms•cm ASTM D257

介电强度 (0.118 in (3.00 mm)) 410 410 V/mil ASTM D149

(16) (16) (kV/mm)

介电常数 ASTM D150

60 Hz 3.53 3.53

1 kHz 3.53 3.53

1 MHz 3.49 3.49

耗散因数 ASTM D150

60 Hz 2.0E-3 2.0E-3

1 kHz 2.0E-3 2.0E-3

1 MHz 4.0E-3 4.0E-3

可燃性 干燥 调节后的 单位制 测试方法

UL 阻燃等级 UL 94

0.031 in (0.8 mm) V-0 V-0

0.06 in (1.6 mm) V-0 V-0

充模分析 干燥 调节后的 单位制 测试方法

熔体粘度 (752°F (400°C), 1000 sec^-1) 350 350 Pa•s ASTM D3835

注射 干燥(英制) 干燥(公制)

干燥温度 302°F 150°C

干燥时间 4.0hr 4.0hr

料筒后部温度 689°F 365°C

料筒中部温度 700°F 371°C

料筒前部温度 711°F 377°C

射嘴温度 720°F 382°C

模具温度 351 到 399°F 177 到 204°C

注射速度 快速 快速

螺杆压缩比 2.5:1.0 到 3.5:1.0 2.5:1.0 到 3.5:1.0

 

 

 

 

医疗级抗伽马辐射PEEK塑胶原料,医疗级抗伽马辐射聚醚醚酮塑胶原料,医疗级抗伽马辐射PEEK KetaSpire® KT-880 GF30是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，COA原料出厂报告,REACH报告,SVHC报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123   13549213581 肖生    QQ：15397858   微信：13549213581